JIS H3300 C4430 Admiralty Brass

JIS H3300 C4430 Admiralty Brass

We bring forth for our clients an exhaustive gamut of Aluminum Brass Tubes, Aluminum Brass Tubing which is preferred across the globe owing to its superior quality, durability and accurate dimensions. The tubes are manufactured using cutting edge techniques and excellent quality raw materials that are procured from trusted & reliable vendors. To ensure confirmation with the ISO standards, the entire range of Aluminum Brass Tubes is examined by adroit quality controllers before final delivery. Clients can buy these tubes from us at industry leading prices.

Technical Specifications :

Specification :

JIS H3300 C4430 Admiralty Brass

Admiralty Brass Tubes

ASTM B111 C44300

ASME SB111

C44300

BS 2871 Part 3 CZ 111

EN 12451 CuZn28 Sn1As

NFA 51 102

CuZn29Sn1

JIS H 3300 C 4430

Salient features:

Rugged construction

Durable finish standards

Accurate dimensions

Corrosion resistance

Application Areas:

Automobile Industry

General Engineering Purposes

Industrial Refrigeration

Heat Exchanger

Radiator

Condenser Copper Tubes

Evaporator Copper Tubes

Product Details :

Minimum Order Quantity	200 Kilogram
Technique	Cutting Edge
Application	Heat Exchanger,Industrial etc
Shape	Tube
Material	Aluminum And Brass

Other Details :

Standard	BS 2871 PART3	ASTM B 111	DIN 1785	NFA 51 102	JIS H3300	IS 1545
Symbol	CZ 111	C 44300	CuZn28Sn1	CuZn29Sn1	C 4430	CuZn29Sn1As
Cu	70.0-73.0	70.0-73.0	70.0-72.5	70.0-73.0	70.0-73.0	70.0-73.0
Sn	1.0-1.5	0.9-1.2	0.9-1.3	0.9-1.2	0.9-1.2	1.0-1.5
Pb	0.07	0.07	0.07	0.07	0.07	0.07
Ni	–	–	0.1	–	–	–
Fe	0.06	0.06	0.07	0.06	0.06	0.06
Zn	REM’DER	REM’DER	REM’DER	REM’DER	REM’DER	REM’DER
As	0.02-0.06	0.02-0.06	0.02-0.035	0.02-0.06	0.02-0.06	0.02-0.06
P	–	–	0.01	–	–	–
Total Impurities Max.					–
	0.03	–	0.1	0.3	–	0.3
Condition	M	61	F36	–	–	O
	TA	–	F32	–	O	TA
	O	–	–	–	–	D
Yield Strength N/MM2	–	–	140-220	–	–	–
	–	105	100-170	–	–	–
Tensile N/MM2 Minimum	–	310	360	–	–	375 Mpa Max.
	–	–	320	–	314Min.	340 Mpa Min.
	–	–	–	–	–	385 Mpa Min.
Elng’Tion Percent (%) Minimum	–	–	45Min.	–	-.	–
	–	–	55Min.	–	30 Min.	–
Hardness HV5 –	150Min	–	–	–	–	80 Max.
	85-105	–	–	80-120	–	80-105
	75Max.	–	–	–	–	130 Min.
Grain Size mm (75X)	0.05Max.	0.010-0.045	–	0.010-0.045	0.010-0.045	0.010-0.04